JIS G3101 SS400 Structural Steel,SS400 steel grade
IS G 3101 SS400 is one of the most commonly used hot rolled general structural steel. Supplied as plates, sheets, flats, bars, sections etc. They are cheap, excelling in weldability & machinability.
SS400 Mechanical Properties
Density (kg/m3) 7860 Young's Modulus (GPa) 190-210 Tensile Strength (MPa) 400 – 510 MPa Yield Strength (MPa) 205-245 MPa Poisson's ratio 0.26
Brinell Hardness (HB) 160
DIN Equivalents for JIS SS400
17100 St 44-2
ASTM Equivalents for JIS SS400
ASTM A36, ASTM A283 Grade D
EN Equivalents for JIS SS400
EN S275/ BS 43A
SS400 Chemical Composition
As per JIS G 3101, Carbon (C), Silicon (Si) and Manganese (Mn) content are not controlled. Phosphorus (P) 0.05% Max and Sulphur (S) 0.05% Max have to controlled below these levels.
Melting point of SS400 is 1430 Degree Celsius
What is SS400 Steels? SS400 steel is a structural hot Rolled steel in the form of plates, sheets & strips for general structural applications. SS400 is a material grade and designation defined in JIS G 3101 standard. JIS G 3101 is a Japanese material standard for hot Rolled steel plates, sheets, strips for general structural usage. The structural quality hot rolled SS400 steel is more reliable in its tensile strength than SS330 steel.
Dimensional Characteristics of SS400 Steels: The applicable thickness for this SS400 material as defined in the JIS 3101 starts from 6 mm to 120 mm.
he Chemical Composition of SS400 Steels: JIS G 3101 defines the chemical composition of SS400 steels as under:
Carbon (C) is not identified in the standard.
Manganese (Mn) is not identified in the standard.
Maximum percentage of Phosphorous (P) is 0.050 percent.
Maximum percentage of Sulphur (S) is 0.050 percent.
Remaining is iron (Fe) percentage and with few negligible impurities.
Mechanical Properties of SS400 Steels: The tensile strength of the SS400 Steels is expressed in Newton per millimeters and it must be at-least 400 N/mm2 (MPa) and maximum can be 510 N/mm2 (MPa). The yield strength is minimum 205 to minimum 245 N/mm2 (MPa) depending on the thickness. The yield strength for thickness below 16 mm is minimum 245 N/mm2 (MPa) whereas for higher gauges above 100 mm is minimum 205 N/mm2 (MPa). The elongation property of SS400 steel varies with the ranges of thickness. The minimum percentage ranges for elongation is 17% thicknesses till 16 mm, 21% for thicknesses till 40 mm, and 23% greater than 50 mm.
SPHC steel comparison with this grade of SS400 material will show how general structure hot rolled steel differs with commercial quality SPHC steel in chemical composition & mechanical properties.
More about JIS G3101 SS400 Structural Steel,SS400 steel grade,contact email@example.com